Product : Mosi2 Heating Elements
Usage : furnace heating part
Voltage : 110-240v
Feature : Oxidation Resistance
Power(w) : 1w-10000w
Diameter : 6/12mm
Length : 100-1000mm
Special shape : available
Density : 5.8g/cm3
Compressive Strength : 650Mpa
1500 Degree U Shape Mosi2 Heating Elements Oxidation Resistance
Mosi2 Heating Elements introduction :
1. Mosi2 heating element is characterisized by excellent oxidation resistance and very good form stability resulting in long element life. they are typically used in electrical heating elements in industrial furnaces and home appliances.
2. Under the oxidizing atmosphere, the maximum operating temperature is 1800, the resistance of the heating element of silicon molybdenum rod increases rapidly with the temperature increasing, and the resistance value is stable when the temperature is constant.Under normal conditions, the resistance of elements does not change with the service time, so the new and old elements can be mixed.
Mosi2 Heating Elements Replacement
If there is a damaged part found in the process of operation, the first thing you should do is determine its location and get all the combination elements ready. After that, you should separate the wire the damaged element clipped to from the screw which is connected to the generatrix. Then remove the remained refractory wool and pull out the refractory stoppers. Insert the new combination elements into the furnace from its roof. Connect all the wires and get the refractory wool filled, and finally raise the temperature.
Physical property of molybdenum disilicide MoSi2 Rod Heater heating element MoSi2 rod:
Volume Density | Bending Strength | Vickers Hardness | Porosity | Water absorption | Heating Elongation Rate |
5.5g/cm³ | 15-25kg/cm² | (HV)570kg/mm² | 7.4% | 1.2% | 4% |
Chemical Properties of Mosi2 Heating Elements
MoSi2 rod heater oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.
Please tell us the following data of molybdenum disilicide MoSi2 rod heating element when send enquiry to us :
d = the diameter of hot zone ?
c = the diameter of cold zone ?
Le = the length of hot zone ?
Lu = the length of cold zone ?
a=Shank spacing
g=junction length
How many piece of MoSi2 rod heater do you need ?
1500 Degree U Shape Mosi2 Heating Elements Oxidation Resistance Images |
Friendly Links: www.everychina.com
Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们